##Thermal_diffusivity_Avg					
						
##General_information						
#Database	jon_n.mdb					
#Instrument	#LFA_457					
#Identity	QD-2-Samples					
#Date	01/06/2021					
#Material	QG-Bi6O6Se2Cl2					
#Ref_temperature /°C	20					
#Ref_density /(g/cm^3)	7.763					
#Sample	QD-Bi6O6Se2Cl2					
#Type	#Single_layer					
#Coating	None					
#Thickness_RT/mm	2.28					
#Diameter/mm	9.8					
#Sensor	#unknown					
#Beam_enlargement/mm	12.7					
#Laser_filter/mm	100					
#Atmosphere	Vacuum					
#Gas_flow/(ml/min)	0					
#Laboratory	MIF Dry Measurement Lab					
#Operator	Jon Newnham					
#Customer	QG-Bi6O6Se2Cl2					
#Remark_mment	no-graphite					
#Cp_table	#undefined					
#Expansion_table	#undefined					
#Temp_recalib_file	#undefined					
#Purge_gas	0					
#CalcCode	C+p/-/x-x-1					
						
##Results						
#Shot number	#Temperature/°C	#Diffusivity/(mm^2/s)	#Std_Dev/(mm^2/s)		conductiviyt W/mK	error
1..2..3	25.1	0.053	0.005		0.104247545	0.009834674
4..5..6	50.3	0.054	0.003		0.10621448	0.005900804
7..8..9	74.2	0.059	0.001		0.116049154	0.001966935
10..11..12	100.9	0.058	0.001		0.11408222	0.001966935
13..14..15	126	0.056	0		0.11014835	0
16..17..18	151	0.061	0		0.119983024	0
19..20..21	176	0.058	0		0.11408222	0
22..23..24	201.1	0.057	0.001		0.112115285	0.001966935
25..26..27	226.2	0.056	0.002		0.11014835	0.00393387
28..29	251.2	0.055	0.002		0.108181415	0.00393387
30..31	276.2	0.053	0.001		0.104247545	0.001966935
32..33	301	0.056	0.002		0.11014835	0.00393387
34..35..36	274.1	0.059	0.001		0.116049154	0.001966935
37..38..39	249.2	0.059	0.001		0.116049154	0.001966935
40..41..42	224.2	0.058	0.002		0.11408222	0.00393387
43..44..45	199.3	0.057	0		0.112115285	0
46..47..48	174.3	0.055	0.002		0.108181415	0.00393387
49..50..51	149.4	0.054	0.003		0.10621448	0.005900804
52..53..54	124.6	0.052	0.004		0.102280611	0.007867739
55..56..57	100.1	0.051	0.005		0.100313676	0.009834674
58..59	75.6	0.028	0.032		0.055074175	0.062941914
60..61..62	50.2	0.053	0.003		0.104247545	0.005900804